Halloysite nanotubes reinforced polybutylene terephthalate based nanocomposites: mechanical, thermal, structural and morphological characterizations

Basit Öğe Kaydı
dc.contributor.advisorDike, Ali Sinan
dc.contributor.authorŞenyel, Mustafa
dc.date.accessioned2025-01-06T17:12:08Z
dc.date.available2025-01-06T17:12:08Z
dc.date.issued2022
dc.departmentEnstitüler, Lisansüstü Eğitim Enstitüsü, Malzeme Mühendisliği Ana Bilim Dalı
dc.descriptionFen Bilimleri Enstitüsü, Malzeme Mühendisliği Ana Bilim Dalı
dc.description.abstractPolibütilen tereftalat (PBT) nanokompozitler, birlikte dönen çift vidalı ekstrüder kullanılarak iki çeşit Türk halloysit nanotüp (HN) ile eritilerek harmanlanmıştır. Doğal olarak oluşan HN numuneleri, ağırlıkça %1, %3, %5 ve %10 HN bileşimlerinde PBT bazlı kompozitler üretmek için kullanılmıştır. PBT boncuk formunda, Advanit ticari adıyla Adana'da bulunan Sasa Polyester A.Ş.'den temin edilmiştir. Saf ve silan modifikasyonlu HN ise, ESH HNT ve ESH HNT S ticari adlarıyla İstanbul'da bulunan Eczacıbaşı Esan firmasından tedarik edilmiştir. Test numuneleri enjeksiyon kalıplama prosesi ile hazırlanmıştır. Üretilen nanokompozitlerin mekanik, termo-mekanik, termal kararlılık, eriyik akışı, yapısal ve morfolojik özellikleri sırasıyla çekme, darbe ve shore sertlik testleri, dinamik mekanik analiz (DMA), termo-gravimetrik analiz (TGA), erime akış hızı ve özkütle ölçümleri ve taramalı elektron mikroskobu (SEM) yöntemleri kullanılarak tayin edilmiştir. Polimer matris ve takviye malzemesi arasındaki ara yüzey yapışmasını araştırmak için saf ve silan kaplı HN içeren kompozit numunelerin sonuçları karşılaştırılmıştır.
dc.description.abstractPolybutylene terephthalate (PBT) nanocomposites were melt-blended with two types of Turkish halloysite nanotubes (HN) using a co-rotating twin-screw extruder. Naturally occurring HN samples were used to produce PBT-based composites at the HN compositions of 1%, 3%, 5%, and 10% by weight. PBT was purchased as bead form under the trade name of Advanite from Sasa polyester A.Ş., Adana, Turkey. Neat and silane-modified grade of HN was supplied by Eczacıbaşı Esan, İstanbul, Turkey with the trade names of ESH HNT and ESH HNT S, respectively. Test samples were prepared by an injection molding process. Mechanical, thermo-mechanical, thermal stability, melt-flow, structural and morphological properties of the produced nanocomposites were reported using tensile, impact and shore hardness tests, dynamic mechanical analysis (DMA), thermo-gravimetric analysis (TGA), melt flow rate and density measurements and scanning electron microscopy (SEM) methods, respectively. Results of neat and silane coated HN containing composite samples were compared in order to investigate the interfacial adhesion between polymer matrix and reinforcement material.
dc.identifier.endpage73
dc.identifier.startpage1
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=CG8WvdvvxJP04Unr7Yecf_dsjKqFf7erlmdmsuwP62i55JyH8_G-dOH0eTg4ydb2
dc.identifier.urihttps://hdl.handle.net/20.500.14669/307
dc.identifier.yoktezid724398
dc.language.isoen
dc.publisherAdana Alparslan Türkeş Bilim ve Teknoloji Üniversitesi
dc.relation.publicationcategoryTez
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_20241211
dc.subjectPolimer Bilim ve Teknolojisi
dc.subjectPolymer Science and Technology
dc.titleHalloysite nanotubes reinforced polybutylene terephthalate based nanocomposites: mechanical, thermal, structural and morphological characterizations
dc.title.alternativeHalloysit nanotüp takviyeli poibütilen tereftalat bazlı nanokompozitlerin mekanik, termal, yapısal ve morfolojik karakterizasyonları
dc.typeMaster Thesis

Dosyalar

Koleksiyon

Lisansüstü Eğitim Enstitüsü Tez Koleksiyonu